In this study, the effect of C addition on the
corrosion behavior of wire rods of 5.5 mm in diameter
was investigated. The horizontal and vertical cross
sections of the wire rods with 0.7, 0.8, 0.9 C ratio were
taken during the metallographical process. The
microstructure of the examined specimens was examined
by light optical (LOM) and scanning electron
microscopy (SEM). Hardness test of steel containing 0.7-
0.9 C was carried out in shimadzu brand micro hardness
tester. Corrosion tests of the prepared samples were
evaluated according to both the weight loss and the
Potentiodynamic Polarization measurements in 3.5%
NaCl solution. Despite the increased hardness of the
specimens examined, the corrosion resistance decreased.
This can be caused by inclusions in the microstructure.