In this study, the effect of carbon content in the
range of 0,7-0,9 on wear resistance was investigated. The
examined specimens in 5.5 mm diameter are manufactured
with drawing process. Wear tests of the cylindrical samples
with a length of 20 mm were examined in pin-on-disc type
wear tester on counter face of 1.2379 cold work tool steel
under the load of 30-60 N. The weight losses of the samples
examined increase with the increase of carbon content and
hardness. Wear Mechanism is mild wear to oxidative wear.
International Iron & Steel Symposium