Electroless nickel coatings can be preferred in wear resistant applications like firearms with good lubricity properties.
In this study, a widely-used magnesium alloy, AZ91D both as-cast and precipitation-hardened conditions were coated
with nickel phosphorus/nickel boron duplex coatings by the electroless deposition method. Solution treatment (W) of the
alloy was carried out at 415 °C for 22 h in carbon powder followed by water quench at 25 °C. Ageing treatment (T6) of
the solution-treated samples was performed at 216 °C for 6 h. The microstructures, elemental distributions and phase
analysis of the obtained coatings were characterized by scanning electron microscopy (SEM), energy dispersive X-ray
spectrometry (EDS) and X-ray diffraction (XRD) analysis. According to the XRD analysis, the obtained coatings have
an amorphous character and subsequent to this, a crystallization process to the sample is carried out at 350 °C. The friction
and wear properties of the coating are studied by means of ball-on-disc experiments at room temperature under 10N
applied loads at 0.1 m/s sliding speed using alumina balls as counterparts. The friction coefficient of the sample was
compared with each other from friction coefficient-distance graphics. The wear rates were determined by measuring the
depth of the track with an 3D-optical microscope (3D-OM). Characterization of the wear tracks was performed by SEM
and EDS.