GX300CrMo27 samples which were reinforced by Ti-B as 1-2.5 wt% have been produced. The first three samples for each samples
were heat treated at 1000 oC. The specimens’ heat treatment time have been changing between 1, 3 and 6 h. The last sample was not
heat treated for comparison. The abrasive wear tests which have loads of 10, 20 and 30 N was performed to the samples to determine
the abrasive wear characteristic. In addition, SEM images of all samples were taken to examine the effect of reinforcement and heat
treatment on the carbide morphology