In this study, the effect of gas nitration on the wear
behavior of crankshaft was investigated. For this purpose, gas
nitration was applied to crankshaft for 12 hours at 500 ° C, and
hardness and microstructure images were examined. Nitrided
and unnitrided samples were subjected to abrasive wear test
under 20N, 40N and 60N load. While 100Cr6 balls were used as
abrasive, crankshaft with nitriding and unnitriding was used as
counter-material. Nitrided samples have increased wear
resistance by about 20% compared to the wear resistance of
unnitrided crank shaft samples.