In this study, an energy efficiency study has been carried out in a natural gas-fired rolling mill annealing furnace of an industrial establishment. In this context, temperature and flue gas measurements were realized while operating the furnace at the operating conditions and waste heat potential was calculated by using these data. In the calculations waste heat potential was determined as 3,630.31 kW. The electricity generation through an Organic Rankine Cycle system has also been determined by using the waste heat potential.

International Iron & Steel Symposium
UDCS

Fatma Çanka Kılıç Mehmet Önder SERT Muharrem EYİDOĞAN Durmuş KAYA Necmi Ozdemir

Yanma hayatın kaynağı , yanma olmazsa enerji de olmazdı enerji yoksa zaten hayatta olmaz. Bizi harekete geçiren , düşündüren , konuşturan şey de hücrelerimizde meydana gelen yanma değil midir ? Modern teknolojilerin temeli enerji de yanmanın – kontrollü yanmanın bir ürünü değil mi ? Kısaca hayatın kaynağı olarak kontrollü ateş insanlık tarihini değiştiren en büyük keşiflerinden biri ve tartışmasız hayatımızı en fazla etkileyen keşif. Hayatımızı kolaylaştıran bu buluş doğal olarak beraberinde birçok tehlikeleri de getirmiştir. Başlarda kontrol dışına çıkmış yanmanın getirdiği tehlike sadece ısıdan etkilenen tehlikeli durumlardı ancak teknolojik ilerlemeler ve nüfusun artmasıyla insanların yaşam yerleri ,yaşam şekilleri değişti. Değişen şehir yapılaşmaları , evlerin yapıları, evlerin kullanım alanlarındaki değişiklik , kullanılan yalıtım malzemeleri ciddi değişimlere uğradı. Özellikle doğal ürünlerin bırakılıp yerine petrol türevli endüstriyel ürünler evlerin dış ve iç tasarımlarında kullanılmaya başlandıktan sonra yangın kaynaklı tehlikelerin sayısı ve çeşidi de çoğaldı. Son yüzyıllarda yangınlarda alev , ısı kadar yangından ortaya çıkan toksik duman yangın kaynaklı ölümlerin en önemli nedeni haline geldi.

International Combustion Symposium
INCOS2018

Fikret Kir Necmi Ozdemir

AlSi12 alloys and alloys produced by Mg addition at different ratios (1% - 2% and 4%) were manufactured by pressurized casting method. Quartz tubes with an inner diameter of 8 mm were used in the castings of the alloys. All castings were carried out in an argon gas atmosphere. These samples (7 mm x 20 mm) were homogenized at 520 ° C for 6 hours. Samples prepared by standard metallographic procedures were immersed in a jar containing 30 gr/l NaCl + 10 ml/l HCl acid solution and samples were weighed at 2-6-12-24 hours intervals. It is clear that the increased Mg ratio reduces the corrosion resistance of the alloys. The reason for this decrease in corrosion resistance is Mg2Si which is likely to occur after Mg addition. Intermetallic are thought to accelerate corrosion by forming a galvanic couple with the matrix. As a result of the corrosion test, SEM images taken from the surface also support our corrosion graph. Thus, when we look at the samples without Mg addition, it is seen that the surface deformation is very small compared to the samples produced by Mg addition.

International Conference of Advanced Materials and Manufacturing Technologies
ICAMT

Engin ÇEVİK S. Yasin Harun ÇUĞ Necmi Ozdemir R. Yildiz S. Akka