MULTİJET FÜZYON TEKNOLOJİSİ İLE ÜRETİLEN PA12 ESASLI NUMUNELERDE YAZDIRMA YÖNLENDİRMESİNİN MEKANİK ÖZELLİKLERE ETKİSİ
Mehmet Erdi KORKMAZ Mustafa GÜNAY
AbstractIn this study, the effects of raster angle on the behavior under the static load of PA12 base materials which were manufactured by Multi Jet Fusion Technology (MJF) in 3D printer, was investigated. For this purpose, standard tensile and three-point bending test samples were produced by 3D printer at a constant deposit thickness (80 µm), constant infill rate (%100) and different printing orientations (0, o 45 and 90 ). Tensile and three-point bending tests were applied for the samples and the findings was evaluated. Consequently, it was determined that the tensile and bending strength of PA12 base sample o has the highest value in 90-90-90 printing orientation.